20 % Elongation Nickel Copper Alloy N05500 Monel K500 Wire For Oceanographic Engineering
Product Introduction
Monel K500 wire is a nickel based alloy with excellent corrosion resistance and high strength, which is widely used in the field of marine engineering. Its main components include nickel, copper, iron, chromium and other elements. By adding aluminum and titanium, the strength and hardness are greatly improved after aging hardening treatment. In marine engineering, Monel K500 wire is often used to manufacture ship shafts, propeller shafts, pumps, valves and marine structural components, which can effectively resist seawater corrosion and chloride ion erosion and prolong the service life of equipment. In addition, Monel K500 wire also has good fatigue resistance and non-magnetic properties, which is suitable for marine applications requiring non-magnetic materials. It has good processability and can be formed by cold processing and hot processing, but attention should be paid to appropriate heat treatment to enhance mechanical properties. In general, Monel K500 wire provides reliable material solutions for offshore engineering with its excellent performance.
Parameter
Chemical composition:
Nickel (Ni): about 63%
Copper (Cu): about 29.5%
Aluminum (Al): about 2.7%
Titanium (Ti): about 0.6%
Iron (Fe): about 2%
Manganese (Mn): about 1.5%
Silicon (Si): about 0.5%
Carbon (C): up to 0.25%
Physical properties:
Density: about 8.05g/cubic centimeter
Melting point: about 1288-1343 degrees Celsius
Thermal Conductivity: Approximately 17.2 Watts/meter-Kelvin
Linear expansion coefficient: approximately 13.9 x 10^-6 degrees Celsius^-1 (room temperature to 100 degrees Celsius)
Mechanical behavior:
Yield Strength (Tensile Strength): Minimum approximately 790 MPa (80,000 psi)
Tensile Strength: Minimum approximately 1100 MPa (110,000 psi)
Elongation: minimum value is about 20%
| Item | Ni | Cu | Al | Ti | Fe | Mn | S | C | Si |
| Monel K500 | ≥63 | 27-33 | 2.3-3.15 | 0.35-0.85 | ≤2 | ≤1.5 | ≤0.01 | ≤0.25 | ≤0.5 |
| Item | Density | Melting point | Tensile Strength | Yield Strength | Elongation |
| Monel K500 | 8.05 g/cm3 | 1288-1343℃ | 1100 | 790 | 20% |
| Monel K500 | Bar/Rod | Forging | Pipe | Sheet/Strip | Welding Wire |
| Standard | ASTM B864 | AMS4676 | ASTM B865 | ASTM B564 | ErNiCu-7 |
| Size Range (mm) | |
| Wire | 0.5-7.5 |
| Rod/Bar | 8.0-200 |
| Strip | (0.50-2.5)*(5-180) |
| Tube | custom made |
| Plate | custom made |
Specific Applications
Advantages and Characteristics
Contact Us
Email:fbwlau@cnrunlai.com
Oem service:
Welcome customized size
We are experience factory for OEM&ODM service
Related Questions and Answers
1. what material is Monel K500?
Monel K500 is a precipitation hardening nickel copper alloy with excellent corrosion resistance, high strength and toughness.
2. what is the chemical composition of Monel K500 wire ?
Monel K500 is mainly composed of nickel, copper, aluminum, titanium and other elements, with nickel content of 63.0% -70.0%, copper content of 27.0% -33.0%, aluminum content of 2.3% -3.15%, and titanium content of 0.35% -0.85%.
3. what are the mechanical properties of Monel K500?
Monel K500 has tensile strength of 1100 MPa, yield strength of 790 MPa and elongation of 20%.
4. what is the corrosion resistance of Monel K500 wire ?
Monel K500 wire has strong corrosion resistance, especially in seawater, chloride, acid environment and high temperature environment, which can effectively resist oxidation and corrosion.