Inconel 625 Plate 992 Inconel Series Plate 600 601 625 718 X750 Nickel Base Alloy Plate

Inconel 625 Plate 992 Inconel Series Plate 600 601 625 718 X750 Nickel Base Alloy Plate

Inconel Series Plate:

High torsional & axial strength (resists bending and twisting)

Better weight-to-strength ratio due to hollow design

More resistant to compression and bending

Product Introduction

Inconel 601 plate is a Ni Cr Fe based solid solution strengthening alloy with excellent high temperature corrosion resistance and oxidation resistance, which is suitable for the environment below 700 ℃. Its chemical composition includes nickel (58%-63%), chromium (21%-25%) and iron (surplus), as well as a small amount of aluminum (1.0%-1.7%) and carbon (0.10% maximum). Inconel 601 plate has good mechanical properties at room temperature and high temperature, with tensile strength of 650 MPa (annealing treatment), yield strength of 300 MPa and elongation of 30%. It can still maintain good oxidation resistance at temperatures up to 1180 ℃, and can form a dense oxide film even in the process of heating and cooling cycle, so it has high spalling resistance. Inconel 601 plate is widely used in pallets, baskets and fixtures of heat treatment plants, steel wire split annealing and radiation tubes, high-speed gas burners, wire mesh belts in industrial furnaces, isolation tanks in ammonia reforming and catalytic support grids in nitric acid manufacturing, exhaust system components, combustion chambers of solid waste incinerators, pipe supports and soot treatment components, etc.

Parameter

Specific Applications

Inconel 601 plate, as a high-performance nickel based alloy, has excellent high-temperature corrosion resistance and oxidation resistance, and is widely used in the following major industrial fields:

1. Aerospace:It is used to manufacture high-temperature components of aero-engine, such as combustion chamber, turbine blade, etc. these components need to operate in harsh environments such as high temperature, high pressure and strong corrosion for a long time.
2. Chemical industry:It is used to manufacture chemical equipment, such as reactors, heat exchangers, tanks, etc., which work in high temperature and corrosive environment.
3. Nuclear energy:It is used to manufacture structures and components in nuclear reactors and is trusted for its stability in high radiation environments.
4. Energy:It is used to manufacture heat exchangers and condensers in power plants. These equipment need to operate stably in high temperature and corrosive environment for a long time.

Advantages and Characteristics

• Excellent high temperature corrosion resistance:Inconel 601 has excellent oxidation resistance and carbonation resistance in high temperature environment. It can be used for a long time at temperatures up to 1180 ° C. even in the process of severe heating and cooling cycles, it can form a dense oxide film with high spalling resistance.
• Good mechanical properties:Inconel 601 has good mechanical properties at room temperature and high temperature. After annealing, the tensile strength can reach 650 n/mm ², the yield strength can reach 300 n/mm ², and the elongation can reach 30%.
• Excellent fatigue resistance:Inconel 601 has excellent fatigue resistance and can be used for a long time under a wide range of cyclic loads.
• Good processability:Inconel 601 has good cold forming characteristics and can be processed by common processing technologies, such as forging, rolling, bending, etc.
• Excellent weldability:Inconel 601 has good welding performance, low sensitivity to hot cracks during welding, and is not prone to cracks, holes and other defects after welding.

Contact Us

Email:fbwlau@cnrunlai.com

Oem service:
Welcome customized size
We are experience factory for OEM&ODM service

Related Questions and Answers

What is the corrosion resistance of Inconel 601?
Inconel 601 has excellent corrosion resistance, especially in high temperature sulfur atmosphere. Its high chromium and aluminum content enables it to form a dense oxide film at high temperature, which effectively prevents corrosion.

What is the high temperature strength of Inconel 601?
Inconel 601 can still maintain good mechanical properties in high temperature environment. After annealing, the tensile strength can reach 650 n/mm ², the yield strength can reach 300 n/mm ², and the elongation can reach 30%. At 700 ° C, the tensile strength can still be maintained above 500 MPa.

How about the processing performance of Inconel 601?
Inconel 601 has good machinability. Although its high strength makes machining relatively difficult, it can still realize the manufacturing of complex parts through reasonable processing technology and tool selection. In the market, many enterprises have developed special processing tools for Inconel 601 to improve processing efficiency.